Epoxy Zinc-Rich Primer

Recommended Applications
As a primer in a general-purpose anti-rust Coating system, it is suitable for use in municipal steel structures, petrochemical facilities, bridges, power plants, offshore structures, and other industrial plant steel structures.

Basic Properties
As a primer in a supporting Coating system, it is suitable for steel structures in the offshore oil and gas, marine steel structures, bridges, wind power, petroleum, chemical, and construction industries.

Excellent corrosion protection.

Quick-drying properties allow for quick overcoating.

Excellent cutting and welding properties.

Surface Preparation
All surfaces to be painted must be clean, dry, and free of oil and other contaminants. Surfaces must be assessed and prepared in accordance with international standards ISO 8504. Cleanliness Grade: Abrasive blasting to Sa 2.5 (ISO 8501-1:2007).
Roughness: Fine to medium, 40-85 microns, using a suitable abrasive (steel shot/angular sand) in accordance with the international standard ISO 8503-2.

Application Conditions
Substrate temperature must not fall below -5°C and must be at least 3°C ​​above the air dew point. Temperature and relative humidity should be measured near the substrate. Good ventilation is generally required in confined areas to ensure proper drying.
When applying the secondary Paint, the paint surface must be dry and free of contamination.

Product Compatibility
Primer: Epoxy zinc primer
Recommended subsequent Coatings: Epoxy high-build paint, epoxy micaceous iron paint, chlorinated rubber paint, vinyl chloride paint, polyurethane Topcoat, acrylic paint, polysiloxane Topcoat, fluorocarbon Topcoat, etc.

Storage
Must be stored in accordance with national regulations. The recommended storage temperature is 15-25°C. Store in a dry and well-ventilated environment. Keep the container tightly closed. Shelf life: 12 months at room temperature.

Packaging
Part A: 30 kg (base), Part B: 3 kg (curing agent).