Key Features
Serves as an anticorrosive primer for various corrosive environments; Features excellent abrasion and impact resistance; Provides outstanding self-healing properties; Good compatibility with various topcoats, including Epoxy, Polyurethane, Chlorinated Rubber, and Single-Component Acrylic; Zero VOCs (Volatile Organic Compounds) and odorless; Fast drying with short recoating interval.
Recommended Use
Recommended as a general, high-performance anticorrosive primer for structural steel in bridges, storage tanks, pipelines, offshore structures, and port machinery. It can also be applied as a single, complete long-term protective coating system on steel surfaces in medium-to-severe corrosive environments and areas subject to high wear.
| Technical Specifications |
| Color |
Zinc Gray |
| Volume Solids (%) |
65 |
| Specific Gravity |
3.1 kg/L |
| Flash Point |
Non-flammable |
| Volatile Organic Compound Content |
0 |
| Water Resistance |
Very Good |
| Abrasion Resistance |
Excellent |
| Solvent Resistance |
Excellent |
| Chemical Resistance |
Excellent (pH range: 6-10) |
| Film thickness and coating rate |
|
Minimum |
Maximum |
Typical |
| Dry Film Thickness (μm) |
50 |
100 |
75 |
| Wet Film Thickness (μm) |
80 |
160 |
120 |
| Theoretical Spreading Rate (m²/kg) |
4.2 |
2.4 |
2.7 |
| Application Methods |
| Spraying |
It is recommended to use the conventional spraying or the HVLP method |
| Brushing |
Recommended for touch-up repairs |
| Construction Parameters |
| Mix Ratio (by weight) |
Component A: Component B = 12:32 |
| Mixing |
Slowly add Component B (powder) to Component A (liquid), stir slowly and thoroughly with a power mixer until uniform, then filter through a 60-mesh sieve. It is recommended to keep stirring continuously during construction to avoid paint sedimentation. |
| Pot Life (at 25°C) |
5 hours (shortens as temperature rises). |
| Thinner/Cleaner |
Water, added in an amount generally not exceeding 5% of the total coating quantity. |
| Guidance Data for Spraying |
|
| Nozzle Pressure |
0.3 – 0.5 MPa (3 – 5kp/cm², 42 – 70 psi). |
| Nozzle Diameter |
1.08 – 1.8 mm (0.043 – 0.072”). |
| Spray Width |
40 – 80° |
| Precautions |
To ensure daily cleaning of the coating system, improve production efficiency, and stable coating quality, it is recommended to rinse the entire spraying equipment system with clean water for several minutes before and after applying water-based inorganic zinc-rich coatings. Additionally, use a mechanical stirring device to keep stirring continuously throughout the construction process. |
| Substrate Temperature |
|
5℃ |
10℃ |
23℃ |
40℃ |
| Tack Free Time |
1.5 hours |
30 minutes |
15 minutes |
5 minutes |
| Hard Dry Time |
2 hours |
80 minutes |
30 minutes |
20 minutes |
| Minimum Recoat Time |
12 hours |
7 hours |
4 hours |
2 hours |